<> "The repository administrator has not yet configured an RDF license."^^ . <> . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo"^^ . "The Fe-Al-Mn-Mo alloy is an alloy steel that is included in the stainless steel class which\r\nreplaces the conventional stainless steel Fe-Cr-Ni alloy. The hardness of the Fe-Al-Mn-Mo alloy\r\nis still lacking because there is still a lot of ferrite structure, the Deep Cryogenic Treatment (DCT)\r\nprocess is carried out to increase the hardness. This study aims to study the effect of DCT\r\nprocessing time on the microstructure, wear and corrosion resistance of Fe-Al-Mn-Mo alloys.\r\nThe process used was DCT by immersion in liquid nitrogen at a temperature (-196℃) with time\r\nvariations of 1, 2, 3, 4, and 5 hours. Then return to room temperature. The results of the chemical\r\ncomposition test showed that the Fe-Al-Mn-Mo alloy had 76.52% Fe as the main element, 14.11%\r\nMn as the main alloy, 10.62% Al and 0.45% Mo, while the Fe- Al-Mn-Mo is a high alloy steel.\r\nThe results of the microstructure test showed that the Fe-Al-Mn-Mo alloy has a ferrite and austenite structure. The DCT process causes the ferrite structure to get bigger while the austenite\r\nstructure gets smaller but the austenite grains will spread more and more between the ferrite\r\ngrains. The Fe-Al-Mn-Mo alloy has a corrosion resistance value of 0.03 mpy and the highest\r\nvalue of corrosion resistance in the 5 hour DCT process is 0.0152 mpy. The Fe-Al-Mn-Mo alloy\r\nhas a wear rate of 0.00032 mm³/kg.m and the lowest value in the 5 hour DCT process is 0.00011\r\nmm³/kg.m = Paduan Fe-Al-Mn-Mo merupakan baja paduan yang termasuk dalam baja tahan karat\r\nyang menggantikan baja tahan karat konvensional paduan Fe-Cr-Ni. Kekerasan paduan Fe-AlMn-Mo masih kurang karena masih banyak struktur ferit, proses Deep Cryogenic Treatment\r\n(DCT) dilakukan untuk meningkatkan kekerasan. Penelitian ini bertujuan untuk mempelajari\r\npengaruh waktu proses DCT terhadap struktur mikro, keausan, dan ketahanan korosi pada\r\npaduan Fe-Al-Mn-Mo. Proses yang dilakukan adalah DCT dengan cara perendaman dalam\r\nnitrogen cair pada suhu (-196℃) dengan variasi waktu 1, 2, 3, 4, dan 5 jam. Lalu dikembalikkan\r\npada suhu ruangan. Hasil uji komposisi kimia menunjukkan paduan Fe-Al-Mn-Mo memiliki\r\nunsur utama Fe sebesar 76,52%, unsur paduan utama Mn sebesar 14,11%, Al sebesar 10,62%\r\ndan Mo sebesar 0,45% sedangkan paduan Fe-Al-Mn-Mo termasuk baja paduan tinggi. Hasil\r\nuji struktur mikro menunjukkan paduan Fe-Al-Mn-Mo memiliki struktur ferit dan austenite.\r\nProses DCT menyebabkan struktur ferit semakin besar sedangkan struktur austenite semakin\r\nkecil namun butir austenite akan semakin menyebar di antara butir ferit. Paduan Fe-Al-Mn-Mo\r\nmemiliki nilai ketahanan korosi sebesar 0,0300 mpy dan nilai tertinggi ketahanan korosi pada\r\nproses DCT 5 jam sebesar 0,0152 mpy. Paduan Fe-Al-Mn-Mo memiliki nilai laju keausan\r\nsebesar 0,00032 mm³/kg.m dan nilai terendah pada proses DCT 5 jam sebesar 0,00011\r\nmm³/kg.m."^^ . "2022-11-28" . . . . . . . . . . . . "Institut Teknologi Nasional Yogyakarta"^^ . . . "Fakultas Teknik dan Perencanaan : Teknik Mesin, Institut Teknologi Nasional Yogyakarta"^^ . . . . . . . . . . . "GALAH"^^ . "JALADRI"^^ . "GALAH JALADRI"^^ . . "Ratna"^^ . "Kartikasari"^^ . "Ratna Kartikasari"^^ . . "Joko"^^ . "Pitoyo"^^ . "Joko Pitoyo"^^ . . . . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "cover-galah jld_merged.pdf"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . . "DAFTAR PUSTAKA GALAH.pdf"^^ . . . "Pengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan\r\ndan ketahanan korosi paduan Fe-Al-Mn-Mo (Text)"^^ . . "HTML Summary of #5618 \n\nPengaruh waktu proses deep cryogenic treatment terhadap struktur mikro, keausan \ndan ketahanan korosi paduan Fe-Al-Mn-Mo\n\n" . "text/html" . . . "TJ Mechanical engineering and machinery"@en . .