creators_name: Arifin, Ahmad Zainal
title: PENGARUH WAKTU PERENDAMAN DEEP CRYOGENIC TREATMENT PADUAN Fe-5,62Al-15,14Mn TERHADAP STRUKTUR MIKRO, KEAUSAN, DAN KETAHANAN KOROSI
ispublished: pub
subjects: TJ
keywords: Fe-Al-Mn Alloy, Deep Cryogenic Treatment, material testing
abstract: Fe-5,62Al-15,14Mn alloy is an alloy steel that is included in stainless steel replacing conventional stainless steel with Fe-Cr-Ni alloy. Some applications of Fe-5,62Al-15,14Mn alloy require high ductility and free internal stress. The deep cryogenic treatment (DCT) process is an alternative process that can be done. This study aims to study the effect of DCT immersion time on the microstructure and mechanical properties of Fe-5,62Al-15,14Mn alloy.
The material used in this research is Fe-5,62Al-15,14Mn alloy steel castings. The composition test is carried out to determine the content contained in the test material, then specimen preparation is carried out. DCT process is carried out by immersion in liquid nitrogen at -196 temperature℃ with a variation of 1, 2, 3, 4, and 5 hours, after which it is refunded at room temperature(warming). The tests carried out were microstructure testing with an optical microscope, wear testing using themethod Ogoshi, and corrosion resistance testing using the weight loss method using a 3.5% NaCl chemical solution for 100 hours.
The results of the chemical composition test show that the percentage of Fe content is 75.60%, Al 5.62%, Mn 15.14% so that it is categorized as high alloy steel. Observation of the microstructure photo shows the structure of austenite, ferrite, and kappa. The highest wear value of Fe-5,62Al-15,14Mn alloy in the process specimen Deep Cryogenic Treatment with an immersion time of 5 hours at 7.6x10-7 mm2/kg and the lowest wear value in the process specimen Deep Cryogenic Treatment with an immersion time of 3 hours at 3.5x10-7 mm2/kg. The highest value of corrosion resistance of Fe-5,62Al-15,14Mn alloy inspecimen is raw material 19.73 mpy and the lowest corrosion rate value is inprocess specimen Deep Cryogenic Treatment with immersion time for 3 hours of 9.55 mpy.
date: 2021-08-06
date_type: published
official_url: https://itny.ac.id
contact_email: library@itny.ac.id
full_text_status: restricted
institution: ITNY
department: Teknik Mesin
thesis_type: other
thesis_name: other
referencetext: ASM Handbook., 1990, Alloy Phase Diagram. ASM International Handbook Committee. Vol. 3.
Allo, B.R., dan Setyanto, D., Pengaruh Cryogenic Terhadap Sifat Mekanis Paduan Aluminium Seri 2024-T3, Jakarta.
Avner, S.H., 1984, Introduction To Physical Metallurgy. McGraw-Hill International Book Company, New York.
Baldissera, P., and Delprete, C., 2008, Deep Cryogenic Treatment: A Bibliographic Review, The Open Mechanical Engineering Journal, Vol. 1-2, Hal : 1-11.
Baldissera, P., and Delprete, C., 2010, Deep Cryogenic Treatment Of AISI 302 stainless steel: Part II– Fatigue and corrosion, Mater, Des, Vol. 31, No. 10, pp. 4731-4737.
Cardarelli, F., 2008, Materials Handbook A Concise Desktop Referenc, Second Edittion, London.
Chastain, S.D., 2004, Metal Casting: A Sand Casting Manual for the Small Foundry, Vol. 2, Chastain Publishing, Jacksonville.
Chiou, S.T., Cheng, W.C., and Lee, W.S., 2004, The Analysis Of The Microstructure Changes Of A Fe-Mn-Al Alloy Under Dynamic Impact Tests, Materials Science and Engineering A 386 : 460-467.
Fontana, G.M., 1987, Corrosion Engineering, 3th ed., McGraw Hill Inc., Singapore.
Gunawan, E., 2017, Pengaruh Temperatur Pada Proses Perlakuan Panas Baja Tahan Karat Martensitik AISI 431 Terhadap Laju Korosi dan Struktur Mikro, Vol. 1, No. 1, Hal : 55-56, Sidoarjo.
Hasananto, N., 2015, Analisis Perbandingan Metode Peningkatan Wear Resistance. Jurnal Rekayasa Mesin, Vol. 6, No.3, Hal : 153-156, Malang.
Hussein, A., 2012, Effect Of Cryogenic Treatment On The Properties Of Low Carbon A858 Steel, Journal of Engineering, Vol. 7, Hal. 18.
Jones, D.A., 1996, Principles and Prevention Of Corrosion, Prentice-Hall International, London.
Kartikasari, R., 2009, Pengaruh Temperatur Temper Terhadap Sifat Mekanik dan Ketahanan Korosi Pada Paduan Fe-1,26Al-0,5C, Media Mesin, Vol. 10, No. 1, Hal : 22-29, Yogyakarta.
Kartikasari, R., dan Sutrisna., 2012, Pengaruh Kadar Si Terhadap Struktur Mikro dan Sifat Mekanik Kandidat Baja Ringan Paduan Fe-7,5Al-5Mn, Rekayasa Teknologi Industri dan Informatika, Yogyakarta.
Kartikasari, R., Sutrisna., dan Batseran, P.W., 2013, Pengaruh Temperatur Anil Terhadap Ketangguhan dan Ketahanan Korosi Kandidat Baja Ringan Paduan Fe-Al-Mn-Si, Rekayasa Teknologi Industri dan Informasi, Vol. 15, No. 1, Hal : 11-15, Yogyakarta.
Kartikasari, R., 2014, Pengaruh Kandungan Aluminium Pada Mikrostruktur dan Perilaku Korosi Baja Ringan Paduan Fe-Al-C cor, Rotasi, Vol. 9, No. 13, Hal : 2241-2249, Yogyakarta.
Kubaschewski, O., 1982, Iron-Binary Phase Diagrams, Berlin.
Łyszkowski, R., Bystrzycki, J., Hot Deformation and Processing Maps Of A Fe–Al Intermetallic Alloy, Materials Characterization, Vol. 96, Hal : 196–205.
Meng, F., Tagashira, K. dan Sohma, H., 1994, Ketahanan Aus dan Mikrostruktur Baja Bantalan Fe-1.4Cr-1C yang Diolah Kriogenik, Vol. 31, No. 7, Hal : 865–868.
Nadig, D.S., 2017, Effects of Cryogenic Treatment on the Strength Properties of Heat Resistant Stainless Steel (07X16H6),IOP Conference Series: Materials Science and Engineering, vol : 229 doi:10.1088/1757899X/229/1/012014.
Nugroho, P.J., 2015, Pengaruh Waktu Kecepatan Pendinginan Pada Besi Cor Inokulasi Whisker Terhadap Struktur Mikro dan Sifat Mekanis, Surakarta.
Patil, P.I, and Kumar, B., 2014, Deep Cryogenic Treatment Of Alloy Steels : A Review, International Journal of Electronics, Communication & Soft Computing Science and Engineering 2.
Raghavan, V., 2005, Fe-Al-Mn, Journal Of Phase Equilibria and Diffusion.
Ratia, V., 2016, Behavior of martensitic wear resistant steels in abrasion and impact wear testing conditions, Tribologia dissertation, Vol. 34.
Seol, J.B., Raabe, D., Choi, P., Park, H.S., Kwak, J.H., Park, C.G., 2012, Direct Evidence For The Formation Of Ordered Carbides In A Ferrite-Based Low-Density Fe-Mn-Al-C Alloy Studied By Transmission Electron Microscopy and Atom Probe Tomography, Scripta Materialia 68: 348–353.
Smallman, RE., 2000, Metalurgi Fisik Modern dan Rekayasa Material, ed VI, Gramedia, Jakarta.
Su, C.W., Lee, J.W., Wang, C.S., Chao, C.G., Liu, T.F., 2007, The Effect Of Hot-Dipped Aluminum Coatings On Fe-8Al- 30Mn-0.8C Alloy, Surface & Coatings Technology 202: 1847–1852.
Van Vlack, L.H., 1992, Ilmu dan Teknologi Bahan, Edisi Kelima Erlangga, Jakarta.
Xuan, F.Z., Huang, X., and Tu, S.T., 2008, Perbandingan Baja Rotor 30Cr2Ni4MoV Dengan Perlakuan Berbeda Terhadap Ketahanan Korosi Dalam Air Suhu Tinggi, Mater Des, Vol. 29, No. 8, Hal : 1533-1539.
Yang., Fuqiang., Song., Renbo., Li., Yaping., Sun., Ting., Wang., Kaikun., 2015, Tensile Deformation Of Low Density Duplex Fe–Mn–Al–C steel, Materials and Design 76 : 32-39.
Yogantoro, A., 2010, Penelitian Pengaruh Variasi Temperatur Pemanasan Low Tempering, dan High Tempering Pada Medium Carbon Steel Produksi Pengecoran Batur Klater Terhadap Struktur Mikro, Kekerasan, dan Ketangguhan, Jurnal Ilmiah Cendekia Eksakta, Hal : 18-23, Surakarta.
citation:   Arifin, Ahmad Zainal  (2021) PENGARUH WAKTU PERENDAMAN DEEP CRYOGENIC TREATMENT PADUAN Fe-5,62Al-15,14Mn TERHADAP STRUKTUR MIKRO, KEAUSAN, DAN KETAHANAN KOROSI.  Other thesis, ITNY.   
document_url: https://repository.itny.ac.id/id/eprint/3195/1/Abstrak.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/2/Bab%20I.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/3/Bab%20II.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/4/Bab%20III.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/5/Bab%20IV.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/6/Bab%20V.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/7/Cover.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/8/Daaftar%20tabel.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/9/Daftar%20gambar.pdf
document_url: https://repository.itny.ac.id/id/eprint/3195/10/Daftar%20isi.pdf