title: Mechanical Properties and Sensitization Behavior of  as Cast Fe-Al-Mn-xSi-C Lightweight Steel
creator: Kartikasari, Ratna
creator: Sutrisna, Sutrisna
subject: TJ Mechanical engineering and machinery
subject: TN Mining engineering. Metallurgy
description: Mechanical properties and sensitization behavior of Fe-Al-Mn-xSi-C alloys  have been investigated by using tensile test, Vickers hardness test, impact test,  scanning electron microscope and XRD. The aim of the research is to  investigate mechanical properties and sensitization behavior of the as cast FeAl-Mn-xSi-Calloys. The alloys were prepared by an induction furnace under  an argon atmosphere. The results showed that the mechanical properties such  as the ultimate tensile test (UTS) and elongation of these alloys were in the  range (617.78-695.56 MPa) and 20.8-30.65% respectively. The hardness of  these alloys was in the range of VHN 220-230. The Charpy impacts of these  alloys were in the range 20-30 J. The microstructures of Fe-Al-Mn-xSi-C  alloys were ɣ phase containing α phase dispersion and were not modified after  sensitization at 1000  oC for 60 minutes.  Keywords: sensitization; as ca
publisher: Research India Publications
date: 2012
type: Article
type: PeerReviewed
format: text
language: en
identifier: https://repository.itny.ac.id/id/eprint/2886/1/Mechanical%20Properties%20and%20Sensitization%20Behavior%20of%20as%20Cast%20Fe-Al-Mn-xSi-C%20Lightweight%20Steel.pdf
identifier:   Kartikasari, Ratna and Sutrisna, Sutrisna  (2012) Mechanical Properties and Sensitization Behavior of as Cast Fe-Al-Mn-xSi-C Lightweight Steel.  International Journal of Advanced Materials Science, 3 (4): 3.  pp. 325-332.  ISSN 2231-1211     
relation: http://www.ripublication.com/ijams.htm